PC LEXAN™  BPL1000-701 SABIC INNOVATIVE NANSHA

193
  • Unit Price:US$ 4,284 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    25MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:UV resistance｜Hydrolysis resistance
  • Application Areas:Automotive components｜Electronic and electrical accessories｜Thin walled products
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength23°CISO 179/1eA18 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A12 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A18 kJ/m²
Dart impact23°C,TotalEnergyASTM D376348.6 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.45mmUL 94V-2
UL flame retardant rating0.8mmUL 94V-0
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13800 °C
Extreme Oxygen IndexISO 4589-236 %
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusASTM D6382680 Mpa
Tensile modulusISO 527-2/12460 Mpa
tensile strengthYieldASTM D63863.4 Mpa
tensile strengthYieldISO 527-2/5064.8 Mpa
tensile strengthBreakASTM D63851.0 Mpa
tensile strengthBreakISO 527-2/5053.5 Mpa
elongationYieldASTM D6384.8 %
Tensile strainYieldISO 527-2/504.7 %
elongationBreakASTM D63896 %
Tensile strainBreakISO 527-2/5097 %
Bending modulus50.0mmSpanASTM D7902670 Mpa
Bending modulusISO 1782370 Mpa
bending strengthISO 17894.8 Mpa
bending strengthYield,50.0mmSpanASTM D790102 Mpa
thermal performanceTest ConditionTest MethodTest Result
RTI StrUL 74680.0 °C
Vicat softening temperatureASTM D152511111 °C
Vicat softening temperature--ISO 306/B50113 °C
Vicat softening temperature--ISO 306/B120114 °C
Ball Pressure Test75°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：-40to40°CASTME8317E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-27E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8317E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-27E-05 cm/cm/°C
RTI ElecUL 74680.0 °C
RTI ImpUL 74680.0 °C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648106 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af96.1 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2kgASTM D123825 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113323.2 cm3/10min
Shrinkage rateMD：--2Internal Method0.50-0.70 %
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Shrinkage rateTD：3.20mmInternal Method0.50-0.70 %
Water absorption rateSaturation,23°CISO 620.35 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dielectric strength1.60mm,inOilASTM D14927 KV/mm
Relative permittivity50HzIEC 602503.00
Relative permittivity60HzIEC 602503.00
Relative permittivity1MHzIEC 602502.90
Dissipation factor50HzIEC 602500.030
Dissipation factor60HzIEC 602500.030
Dissipation factor1MHzIEC 602500.010
Compared to the anti leakage trace indexIEC 60112PLC 3
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.