ABS

ABS MAGNUM™ 8391 MED TRINSEO NETHERLANDS

281

Unit Price:US$ 6,476 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Medical grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA3	18.0 kJ/m²
	Charpy Notched Impact Strength	23°C		NoBreak
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C		NoBreak

flammability	Test Condition	Test Method	Test Result
Normal combustion performance with a thickness of 1.6mm	1.50mm,UL	J	HB
Burning rate	2.00mm	ISO 3795	60 mm/min
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ASTM D638	35.0 Mpa
elongation	Yield	ASTM D638	2.7 %
Tensile strain	Yield,3.20mm,Injection	ISO 527-2/50	2.5 %
Tensile strain	Tensile strain	Yield,3.20mm,Injection	ISO 527-2/100	2.6 %
elongation	Break	ASTM D638	8.7 %
Nominal fracture strain		ISO 527-23	20 %
Bending modulus		ASTM D790	2480 Mpa
Bending modulus	Bending modulus	3.20mm,InjectionMolded	ISO 178	2400 Mpa
bending strength		ASTM D790	75.0 Mpa
bending strength	bending strength	3.20mm,InjectionMolded	ISO 178	70.0 Mpa
Tensile modulus	3.20mm,Injection	ISO 527-2	2340 Mpa
Tensile modulus	Tensile modulus		ISO 527-23	2400 Mpa
tensile strength	Yield	ASTM D638	48.0 Mpa
	tensile strength	Yield,3.20mm,Injection	ISO 527-2/50	45.0 Mpa
		tensile strength	Yield,3.20mm,Injection	ISO 527-2/100	47.0 Mpa
		tensile strength	tensile strength	Yield	ISO 527-23	48.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	87.0 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	74.0 °C
		Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	95.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa	ISO 75-23	95.0 °C
Vicat softening temperature		ASTM D15258	99.0 °C
	Vicat softening temperature		ISO 306/B50	95.0 °C
	Vicat softening temperature	Vicat softening temperature	50N	ISO 3063	92.0 °C

Physical properties	Test Condition	Test Method	Test Result
Apparent density		ISO 60	0.65 g/cm³
melt mass-flow rate	220°C/10.0kg	ASTM D1238	28 g/10min
	melt mass-flow rate	230°C/3.8kg	ASTM D1238	8.0 g/10min
	melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	28 g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	IEC 60093	27.0 cm3/10min
Shrinkage rate	MD	ASTM D955	0.40-0.70 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.40-0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	108

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.