Material Description

Material Properties:Thermal stability
Application Areas:Home appliance components｜Electronic and electrical components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	14 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	75 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	95 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	12 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	14 kJ/m²

flammability	Test Condition	Test Method	Test Result
Flammability level		UL 94	HB
Flammability level	Flammability level		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--	ISO 527-2	13000 Mpa
	Tensile modulus	120°C	ISO 527-2	6900 Mpa
		Tensile modulus	160°C	ISO 527-2	6100 Mpa
			Tensile modulus	180°C	ISO 527-2	5700 Mpa
			Tensile modulus	Tensile modulus	200°C	ISO 527-2	5300 Mpa
tensile strength	Break	ISO 527-2	230 Mpa
	tensile strength	Break, 120°C	ISO 527-2	130 Mpa
		tensile strength	Break, 160°C	ISO 527-2	115 Mpa
			tensile strength	Break, 180°C	ISO 527-2	105 Mpa
			tensile strength	tensile strength	Break, 200°C	ISO 527-2	100 Mpa
Tensile strain	Break	ISO 527-2	3.0 %
	Tensile strain	Break, 120°C	ISO 527-2	6.5 %
		Tensile strain	Break, 160°C	ISO 527-2	6.5 %
			Tensile strain	Break, 180°C	ISO 527-2	6.5 %
			Tensile strain	Tensile strain	Break, 200°C	ISO 527-2	6.5 %
Bending modulus	--	ISO 178	11500 Mpa
	Bending modulus	120°C	ISO 178	5800 Mpa
	Bending modulus	Bending modulus	160°C	ISO 178	5200 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	290 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	290 °C
Melting temperature		ISO 11357-3	295 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	5.0E-5 cm/cm/°C
RTI Elec	1.5 mm	UL 746	65.0 °C
Thermal Index - 5000 hr		IEC 60216	177 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.51 g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.50 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.2 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	1.0E+14 ohms·cm
Dielectric strength		IEC 60243-1	30 KV/mm
Relative permittivity	100 Hz	IEC 60250	4.30
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	4.00
Compared to the anti leakage trace index		IEC 60112	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.