Material Description

Material Properties:High mobility｜flexibility｜Flame retardant
Application Areas:Automotive Applications
Color:--
Grade:--

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result
Melt viscosity	200°C, 1000 sec^-1	ASTM D3835	310 Pa·s

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	41.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	2.3 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.5 mm	UL 94	5VB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2410 Mpa
tensile strength	Yield	ASTM D638	42.0 Mpa
tensile strength	tensile strength	Break	ASTM D638	35.0 Mpa
elongation	Yield	ASTM D638	2.1 %
elongation	elongation	Break	ASTM D638	11 %
Bending modulus	50.0 mm Span	ASTM D790	2720 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	73.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 to 90 °C
drying time			2.0 to 4.0 hr
Suggested maximum moisture content			0.10 %
Suggested injection volume			50 to 70 %
Temperature at the rear of the barrel			170 to 180 °C
Temperature in the middle of the barrel			195 to 205 °C
Temperature at the front of the material cylinder			200 to 215 °C
Spray nozzle temperature			200 to 220 °C
Processing (melt) temperature			200 to 220 °C
Mold temperature			50 to 70 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			30 to 60 rpm
Exhaust hole depth			0.038 to 0.051 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	83.0 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	72.0 °C
Vicat softening temperature		ASTM D15255	90.0 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.9E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.9E-5 cm/cm/°C
RTI Elec		UL 746	60.0 °C
RTI Imp		UL 746	60.0 °C
RTI		UL 746	60.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	230°C/3.8 kg	ASTM D1238	6.8 g/10 min
melt mass-flow rate	melt mass-flow rate	220°C/5.0 kg	ISO 1133	9.0 g/10 min
Melt Volume Flow Rate (MVR)	220°C/10.0 kg	ISO 1133	37.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.