PA66 Ultramid® A3EG6 BASF GERMANY

404

Unit Price:US$ 3,525 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
187MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PA66 Ultramid® A3EG6 BASF SHANGHAI

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜Oil resistant｜dimensional stability
Application Areas:machine｜Mechanical components｜Shell｜Electrical components｜Electronic insulation
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			玻纤增强注射级.用于需要高刚性和尺寸稳定性的机械部件护罩.插座外罩.冷却风扇.汽车冷却系统水室以及电绝缘制品

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179	70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	85 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	3.0mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	6.0mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ASTM D256/ISO 179	13/22 kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	11 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	3/5 %
tensile strength		ASTM D638/ISO 527	10000/7200 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	8600/7000 kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	280/220 kg·cm/cm(J/M)ft·lb/in
Tensile modulus	23°C	ISO 527-2	10000 Mpa
tensile strength	Break,23°C	ASTM D638	186 Mpa
	tensile strength	Break,-40°C	ISO 527-2	238 Mpa
	tensile strength	tensile strength	Break,23°C	ISO 527-2	190 Mpa
elongation	Break,23°C	ASTM D638	3.0 %
Tensile strain	Break,-40°C	ISO 527-2	3.2 %
Tensile strain	Tensile strain	Break,23°C	ISO 527-2	3.0 %
Bending modulus	23°C	ISO 178	8600 Mpa
bending strength	23°C	ISO 178	280 Mpa

thermal performance	Test Condition	Test Method	Test Result
Combustibility (rate)		UL 94	94HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	250 1.8Mpa ℃（℉）
Melting temperature			260 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	1.5-2/6-7 mm/mm.℃
RTI Imp	6.0mm	UL 746	120 °C
RTI Str	1.5mm	UL 746	130 °C
	RTI Str	3.0mm	UL 746	130 °C
	RTI Str	RTI Str	6.0mm	UL 746	130 °C
Melting temperature		ISO 3146	260 °C
Linear coefficient of thermal expansion	MD	ASTME831	1E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD		2.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD		6.5E-05 cm/cm/°C
RTI Elec	0.75mm	UL 746	120 °C
	RTI Elec	1.5mm	UL 746	120 °C
		RTI Elec	3.0mm	UL 746	120 °C
		RTI Elec	RTI Elec	6.0mm	UL 746	120 °C
RTI Imp	1.5mm	UL 746	120 °C
RTI Imp	RTI Imp	3.0mm	UL 746	120 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	250 °C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	250 °C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	250 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250 °C
Melting temperature		ASTM D3418	260 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.36
melt mass-flow rate		ASTM D1238/ISO 1133	40 g/10min
Water absorption rate		ASTM D570/ISO 62	5.2-5.8 %
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	40.0 cm3/10min
Shrinkage rate	MD：3.18mm		0.30 %
Water absorption rate	Saturation	ASTM D570	5.5 %
	Water absorption rate	Saturation,23°C	ISO 62	5.5 %
		Water absorption rate	Equilibrium,50%RH	ASTM D570	1.7 %
		Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.7 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257/IEC 60093	10^12/10^10 Ω
Dielectric constant		ASTM D150/IEC 60250	3.6/5.6
Volume resistivity		ASTM D257/IEC 60093	10^15/10^12 Ω.cm
	Volume resistivity	1.50mm	ASTM D257	1E+13 ohms·cm
	Volume resistivity	Volume resistivity		IEC 60093	1E+13 ohms·cm
Dielectric constant	1MHz	IEC 60250	3.50
Dissipation factor	100Hz	IEC 60250	0.014
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.014
Compared to the anti leakage trace index		IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Ultramid® A3EG6 BASF GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet