Material Description

Material Properties:Flame retardant｜High mobility
Application Areas:Automotive Applications｜Lighting installation｜electrical equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5300 N
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C,Complete Break	ISO 7391	12 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,Partial Break	ISO 7391	65 kJ/m²
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	60.0 J

flammability	Test Condition	Test Method	Test Result
FlashIgnitionTemperature		ASTM D1929	480 °C
SelfIgnition		ASTM D1929	550 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2/1	2400 Mpa
tensile strength	Yield,23°C	ISO 527-2/50	67.0 Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/50	75.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	6.1 %
Tensile strain	Tensile strain	Break,23°C	ISO 527-2/50	130 %
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	133 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	121 °C
Vicat softening temperature		ISO 306/B50	143 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	6.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Apparent density		ISO 60	0.66 g/cm³
melt mass-flow rate	300°C/1.2kg	ISO 1133	13 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	12.0 cm3/10min
Shrinkage rate	TD	ISO 2577	0.60-0.80 %
Shrinkage rate	Shrinkage rate	MD	ISO 2577	0.60-0.80 %
Water absorption rate	Saturation,23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+16 ohms
Volume resistivity	23°C	IEC 60093	1E+16 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC Makrolon® RX2635 COVESTRO SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet