PA66

PA66 LNP™ LUBRILOY™ RF206 BK8115 SABIC INNOVATIVE US

199

Unit Price:US$ 3,295 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:wear resistant｜enhance
Application Areas:Electronic and Electrical Applications｜Outdoor applications｜Lawn garden equipment
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.1 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	35 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	13.3 J
Multi axis Instrumented Impact Energy		ISO 6603-2	3.70 J

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	8770 Mpa
Friction coefficient	Static	ASTM D3702Modified	0.40
Wear factor	Washer	ASTM D3702Modified	45.0 10^-10in^5-min/ft-lb-hr
Tensile modulus		ISO 527-2/1	8470 Mpa
tensile strength	Break	ASTM D638	121 Mpa
tensile strength	tensile strength	Break	ISO 527-2/5	118 Mpa
elongation	Break	ASTM D638	2.5 %
Tensile strain	Break	ISO 527-2/5	2.3 %
Bending modulus	50.0mmSpan	ASTM D790	7060 Mpa
Bending modulus	Bending modulus		ISO 178	7200 Mpa
bending strength		ISO 178	167 Mpa
bending strength	bending strength	Break,50.0mmSpan	ASTM D790	173 Mpa
Friction coefficient	Dynamic	ASTM D3702Modified	0.40

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	258 °C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	252 °C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	241 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	224 °C
Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	3.8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to30°C	ASTM D696	7.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：24hr	ASTM D955	0.60 %
Shrinkage rate	Shrinkage rate	TD：24hr	ASTM D955	1.2 %
Water absorption rate	24hr,50%RH	ASTM D570	0.38 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.66 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 LNP™ LUBRILOY™ RF206 BK8115 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet