Plastic Raw Materials
PC

PC PANLITE® LD-1000RM TEIJIN JAPAN

275
  • Unit Price:US$ 3,363 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    40MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility｜Thermal stability
  • Application Areas:Fitness equipment｜Automotive Applications
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notchISO 179无断裂
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.44mmUL 94V-2
mechanical propertiesTest ConditionTest MethodTest Result
Elongation at BreakASTM D638/ISO 527110 %
Tensile modulusASTM D638/ISO 5272500 kg/cm²(MPa)[Lb/in²]
Bending modulusASTM D790/ISO 1782300 kg/cm²(MPa)[Lb/in²]
bending strengthASTM D790/ISO 17891 kg/cm²(MPa)[Lb/in²]
Tensile strainYieldISO 527-2/506.0 %
Tensile strainBreakISO 527-2/50110 %
tensile strengthBreakISO 527-2/5060.0 Mpa
tensile strengthYieldISO 527-2/5060.0 Mpa
Tensile modulusISO 527-2/12600 Mpa
Bending modulusISO 1782400 Mpa
bending strengthISO 17895.0 Mpa
Bending modulusASTM D-7902450(25000) Mpa(kgf/cm2)
Elongation at BreakBreak点ASTM D-638110 %
tensile strengthYield点ASTM D-63863(640) Mpa(kgf/cm2)
tensile strengthBreak点ASTM D-63865(660) Mpa(kgf/cm2)
bending strengthASTM D-79095(950) Mpa(kgf/cm2)
Impact strength of cantilever beam gap艾氏、带Notched厚度3.2mmASTM D-256780(80) J/m(kgf·cm/cm)
Shrinkage rateFlowASTM D-9550.4-0.6 %
Shrinkage rateAcross FlowASTM D-9550.4-0.6 %
Impact strength of cantilever beam gap艾氏、带Notched厚度6.4mmASTM D-256110(11) J/m(kgf·cm/cm)
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperatureHDTASTM D648/ISO 75125 ℃（℉）
RTI1.5mmUL 746125 °C
RTI Imp1.5mmUL 746115 °C
RTI Elec1.5mmUL 746125 °C
Linear coefficient of thermal expansionTDISO 11359-27E-05 cm/cm/°C
Linear coefficient of thermal expansionASTM D696/ISO 113590.7 mm/mm.℃
Vicat softening temperatureASTM D1525/ISO R306139 ℃（℉）
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B137 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A128 °C
Linear coefficient of thermal expansionFlowASTM D-6967 10-5cm/cm/℃
Linear coefficient of thermal expansionAcross FlowASTM D-6967 10-5cm/cm/℃
Temperature index电学式，厚度1.47mmUL 746B125 °C
Temperature index冲击式，厚度1.47mmUL 746B115 °C
Temperature index非冲击式，厚度1.47mmUL 746B125 °C
Hot deformation temperature负荷1.813MPa(18.6kgf/cm2)JIS K-7207135 °C
Vicat softening temperatureISO 306/B50139 °C
Linear coefficient of thermal expansionMDISO 11359-27E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rate23°C,24hrISO 620.20 %
Shrinkage rateMD:4.00mmInternal Method0.40-0.60 %
Shrinkage rateTD:4.00mmInternal Method0.40-0.60 %
Water absorption rateASTM D570/ISO 620.20 %
Shrinkage rateASTM D9550.4-0.6 %
densityASTM D792/ISO 11831280
Transmittance rate3mm thickASTM D-1003white %
Electrical performanceTest ConditionTest MethodTest Result
Dissipation factor100HzIEC 602501.1E-03
Relative permittivity1MHzIEC 602503.40
Relative permittivity100HzIEC 602503.40
Dielectric strengthIEC 60243-132 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Surface resistivityIEC 60093>1.0E+15 ohms
Compared to the anti leakage trace indexIEC 60112PLC 2
Dissipation factor1MHzIEC 602509E-03
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.