PC/PET

PC/PET XYLEX™ X7507-NA9D032T SABIC INNOVATIVE US

288

Unit Price:US$ 3,797 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
12MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity	2540 μm	ASTM D1003	> 85.0 %
turbidity	2540 μm	ASTM D1003	1.6 %

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	79.0 J

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	2300 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2660 Mpa
tensile strength	Yield3	ASTM D638	61.0 Mpa
	tensile strength	Yield	ISO 527-2/50	62.0 Mpa
		tensile strength	Break3	ASTM D638	65.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	59.0 Mpa
elongation	Yield3	ASTM D638	6.0 %
	elongation	Yield	ISO 527-2/50	5.4 %
		elongation	Break3	ASTM D638	130 %
		elongation	elongation	Break	ISO 527-2/50	110 %
Bending modulus	50.0 mm Span4	ASTM D790	2320 Mpa
Bending modulus	Bending modulus	--5	ISO 178	2180 Mpa
bending strength	--5,6	ISO 178	92.0 Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	96.0 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 to 95 °C
drying time			3.0 to 5.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 80 %
Temperature at the rear of the barrel			240 to 250 °C
Temperature in the middle of the barrel			245 to 265 °C
Temperature at the front of the material cylinder			250 to 270 °C
Spray nozzle temperature			250 to 270 °C
Processing (melt) temperature			250 to 270 °C
Mold temperature			45 to 60 °C
Back pressure			0.200 to 0.500 Mpa
Screw speed			20 to 100 rpm
Exhaust hole depth			0.013 to 0.020 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	104 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	105 °C
Vicat softening temperature	--	ASTM D15259	125 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	127 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.3E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	265°C/2.16 kg	ASTM D1238	8.0 g/10 min
Melt Volume Flow Rate (MVR)	265°C/2.16 kg	ISO 1133	5.00 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.80 %
Water absorption rate	Saturation, 23°C	ISO 62	0.32 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.12 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/PET XYLEX™ X7507-NA9D032T SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet