ABS

ABS STAREX® SF-0505 Samsung Cheil South Korea

267

Unit Price:US$ 2,278 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Thermal stability｜Aging resistance
Application Areas:Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.3 kJ/m²
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	110 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.5 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/50	2400 Mpa
tensile strength	Yield	ASTM D638	50.0 Mpa
	tensile strength	Yield	ISO 527-2/50	56.0 Mpa
		tensile strength	Break	ASTM D638	39.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	48.0 Mpa
elongation	Break	ASTM D638	11 %
Tensile strain	Break	ISO 527-2/50	5.6 %
Bending modulus		ASTM D790	2300 Mpa
Bending modulus	Bending modulus		ISO 178	2400 Mpa
bending strength		ASTM D790	71.0 Mpa
Tensile modulus		ASTM D638	2400 Mpa
bending strength		ISO 178	81.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	73.0 °C
Vicat softening temperature	--	ISO 306/B50	94.0 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	96.0 °C
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	92.0 °C
	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	84.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	84.0 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.11 g/cm³
density	density		ISO 1183	1.11 g/cm³
melt mass-flow rate	220°C/10.0kg	ASTM D1238	17 g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	17 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.30-0.60 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	ISO 2577	0.30-0.60 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	113
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	113
Pencil hardness		JISK5401	F

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS STAREX® SF-0505 Samsung Cheil South Korea

Material Description

Technical Data Sheet Compare

Technical Data Sheet