Material Description

Material Properties:Thermal stability｜High temperature resistance
Application Areas:Home appliance components｜Electrical applications
Color:--
Grade:--

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0 mm	UL 94	V-0
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	0.75 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	89.0 Mpa
Bending modulus		ISO 178	3670 Mpa
Tensile strain	Break	ISO 527-2/5	52 %
tensile strength	Yield	ISO 527-2/5	48.0 Mpa

injection	Test Condition	Test Method	Test Result
Back pressure			0.981 to 3.92 Mpa
Screw speed			< 80 rpm
Mold temperature			60 to 80 °C
Processing (melt) temperature			260 to 300 °C
Spray nozzle temperature			270 to 290 °C
Temperature at the front of the material cylinder			290 to 300 °C
Temperature in the middle of the barrel			270 to 290 °C
Temperature at the rear of the barrel			260 to 270 °C
Suggested maximum moisture content			0.020 %
drying time			3.0 to 4.0 hr
drying temperature			80 to 100 °C

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI Elec		UL 746	80.0 °C
Vicat softening temperature		ISO 306/B50	109 °C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	94.0 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	104 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	260°C/5.0 kg	ISO 1133	11 g/10 min
melt mass-flow rate	melt mass-flow rate	250°C/2.16 kg	ISO 1133	1.8 g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO Lumiloy® GN3101F KA02 LG GUANGZHOU

Material Description

Technical Data Sheet Compare

Technical Data Sheet