PA6

PA6 Ultramid® 8253HS BK102 BASF GERMANY

206

Unit Price:US$ 3,572 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
42MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜high strength｜Oil resistant
Application Areas:Helmet｜Automotive Applications｜Engine parts
Color:--
Grade:Enhanced level

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
Dart impact	23°C	Internal Method	271 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	3.0mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	6.0mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield,23°C	ISO 527-2	60.0 Mpa
elongation	Yield,23°C	ASTM D638	4.0 %
Tensile strain	Yield,23°C	ISO 527-2	4.0 %
elongation	Break,23°C	ASTM D638	>100 %
Nominal tensile fracture strain	23°C	ISO 527-2	40 %
Bending modulus	23°C	ASTM D790	2270 Mpa
Bending modulus	Bending modulus	23°C	ISO 178	1900 Mpa
bending strength	23°C	ASTM D790	85.0 Mpa
bending strength	bending strength	23°C	ISO 178	65.0 Mpa
Tensile modulus	23°C	ISO 527-2	2400 Mpa
tensile strength	Yield,23°C	ASTM D638	65.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	160 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	60.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	55.0 °C
Melting temperature		ASTM D3418	220 °C
Melting temperature	Melting temperature		ISO 3146	220 °C
RTI Imp	6.0mm	UL 746	105 °C
RTI Str	0.71mm	UL 746	95.0 °C
	RTI Str	0.75mm	UL 746	95.0 °C
		RTI Str	1.5mm	UL 746	105 °C
			RTI Str	3.0mm	UL 746	105 °C
			RTI Str	RTI Str	6.0mm	UL 746	105 °C
Linear coefficient of thermal expansion	MD	ASTME831	9.9E-05 cm/cm/°C
RTI Elec	0.71mm	UL 746	105 °C
	RTI Elec	0.75mm	UL 746	105 °C
		RTI Elec	1.5mm	UL 746	105 °C
			RTI Elec	3.0mm	UL 746	105 °C
			RTI Elec	RTI Elec	6.0mm	UL 746	105 °C
RTI Imp	0.71mm	UL 746	95.0 °C
	RTI Imp	0.75mm	UL 746	95.0 °C
		RTI Imp	1.5mm	UL 746	105 °C
		RTI Imp	RTI Imp	3.0mm	UL 746	105 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.18mm		1.2 %
Water absorption rate	24hr	ASTM D570	1.5 %
	Water absorption rate	23°C,24hr	ISO 62	1.5 %
		Water absorption rate	Saturation	ASTM D570	8.1 %
			Water absorption rate	Saturation,23°C	ISO 62	8.1 %
				Water absorption rate	Equilibrium,50%RH	ASTM D570	2.3 %
				Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.3 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	82

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Ultramid® 8253HS BK102 BASF GERMANY

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet