PBT VALOX™ 553-BK1006 SABIC INNOVATIVE US

265

Unit Price:US$ 4,101 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
42MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low warpage｜Glass fiber reinforced
Application Areas:Automotive External Parts｜Construction field｜Outdoor applications｜Electrical appliances｜Plastic bag｜Automotive interior parts｜Casters
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ASTM D4812	640 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	85 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.9mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.3mm	UL 94	5VA
Extreme Oxygen Index		ASTM D2863	37 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ASTM D638	110 Mpa
Bending modulus	50.0mmSpan	ASTM D790	9400 Mpa
bending strength	Break,50.0mmSpan	ASTM D790	179 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Str		UL 746	125 °C
RTI Imp		UL 746	110 °C
RTI Elec		UL 746	125 °C
Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	2.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	2.2E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	160 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	204 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24hr	ASTM D570	0.070 %
Shrinkage rate	TD：--4	Internal Method	0.60-0.90 %
	Shrinkage rate	TD：--3	Internal Method	0.40-0.60 %
		Shrinkage rate	MD：--3	Internal Method	0.30-0.50 %
		Shrinkage rate	Shrinkage rate	MD：--2	Internal Method	0.50-0.80 %
Specific volume		ASTM D792	0.640 cm³/g
density		ASTM D792	1.59 g/cm³
Outdoor applicability		UL 746C	f1

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 1
Arc resistance		ASTM D495	PLC6
Dissipation factor	1MHz	ASTM D150	0.020
Dissipation factor	Dissipation factor	100Hz	ASTM D150	2E-03
Dielectric constant	1MHz	ASTM D150	3.70
Dielectric constant	Dielectric constant	100Hz	ASTM D150	3.80
Dielectric strength	3.20mm,inAir	ASTM D149	19 KV/mm
Dielectric strength	Dielectric strength	1.60mm,in Oil	ASTM D149	26 KV/mm
Volume resistivity		ASTM D257	4.3E+16 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT VALOX™ 553-BK1006 SABIC INNOVATIVE US

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet