Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ASTM D256	85 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ASTM D256	69 J/m
Impact strength of simply supported beam without notch	23°C	ISO 179	59 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	50 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	9.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0mm	UL 94	HB
	UL flame retardant rating	0.69mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ASTM D790	194 Mpa
Bending modulus	23°C	ISO 178	8300 Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	8270 Mpa
Tensile creep modulus	1000hr	ISO 899-1	6700 Mpa
tensile strength	Break,23°C	ISO 527-2	125 Mpa
tensile strength	tensile strength	Break,80°C	ISO 527-2	79.0 Mpa
Tensile modulus	23°C	ISO 527-2	9700 Mpa
tensile strength	Break,23°C	ASTM D638	125 Mpa
	tensile strength	Break,-40°C	ISO 527-2	195 Mpa
		tensile strength	Break,120°C	ISO 527-2	47.0 Mpa
		tensile strength	tensile strength	Break,150°C	ISO 527-2	35.0 Mpa
elongation	Break,23°C	ASTM D638	2.2 %
Tensile strain	Break,-40°C	ISO 527-2	2.4 %
	Tensile strain	Break,23°C	ISO 527-2	2.2 %
		Tensile strain	Break,80°C	ISO 527-2	3.6 %
			Tensile strain	Break,120°C	ISO 527-2	5.9 %
			Tensile strain	Tensile strain	Break,150°C	ISO 527-2	4.8 %
Tensile creep modulus	1hr	ISO 899-1	7600 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Elec	1.5mm	UL 746	130 °C
RTI Elec	RTI Elec	0.69mm	UL 746	130 °C
Linear coefficient of thermal expansion	MD		4E-05 cm/cm/°C
Melting temperature		ISO 3146	223 °C
Melting temperature	Melting temperature		ASTM D3418	223 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	175 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	177 °C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	210 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	210 °C
RTI Imp	0.69mm	UL 746	90.0 °C
RTI Elec	3.0mm	UL 746	130 °C
RTI Str	3.0mm	UL 746	130 °C
RTI Imp	1.5mm	UL 746	90.0 °C
RTI Imp	RTI Imp	3.0mm	UL 746	90.0 °C
RTI Str	0.69mm	UL 746	130 °C
RTI Str	RTI Str	1.5mm	UL 746	130 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	ISO 294-4	0.29 %
	Shrinkage rate	TD	ISO 294-4	0.75 %
	Shrinkage rate	Shrinkage rate	MD：3.18mm		0.30 %
Water absorption rate	Saturation	ASTM D570	0.40 %
Melt Volume Flow Rate (MVR)	275°C/2.16kg	ISO 1133	20.0 cm3/10min
density		ISO 1183	1.47 g/cm³
density	density		ASTM D792	1.47 g/cm³
Water absorption rate	Saturation,23°C	ISO 62	0.40 %
	Water absorption rate	Equilibrium,50%RH	ASTM D570	0.20 %
	Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %
Viscosity value	降低的粘度	ISO 1628	105.0 ml/g

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	1E+14 ohms
Surface resistivity	Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity	1.50mm	ASTM D257	>1.0E+13 ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	>1.0E+13 ohms·cm
Dielectric constant	100Hz	IEC 60250	3.80
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3.70
Dissipation factor	100Hz	IEC 60250	3E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.018
Compared to the anti leakage trace index		IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT Ultradur® S 4090 G6 BASF GERMANY

Material Description

Technical Data Sheet Compare

Technical Data Sheet