POM

POM Delrin® 988P DUPONT USA

218
  • Unit Price:US$ 5,008 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    50MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High temperature resistance｜wear resistant
  • Application Areas:Fitness equipment｜Automotive components
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

Basic PerformanceTest ConditionTest MethodTest Result
Water absorption rate50%相对湿度ASTM D-5700.22 %
Water absorption rate浸渍Equilibrium点ASTM D-5700.90 %
Water absorption rate24hr浸渍ASTM D-5700.25 %
mechanical propertiesTest ConditionTest MethodTest Result
tensile strength122℃ASTM D-63826 Mpa
Izod Notched Impact Strength23℃ASTM D-25671 J/m
Elongation at Break100℃ASTM D-638>260 %
Bending modulus100℃ASTM D-7901030 Mpa
tensile strength100℃ASTM D-63836 Mpa
Bending modulus23℃ASTM D-6383640 Mpa
tensile strength70℃ASTM D-63848 Mpa
Compressive stress23℃，10%变形ASTM D-695121 Mpa
Izod Notched Impact StrengthNotched-40℃ASTM D-25655 J/m
Elongation at Break122℃ASTM D-638>260 %
Elongation at Break-55℃ASTM D-63810 %
Bending modulus70℃ASTM D-7901720 Mpa
Elongation at Break23℃ASTM D-63825 %
Hardness (Rockwell R)ASTM D-785120
Bending deformation23℃ASTM D-79097 Mpa
Bending modulus-55℃ASTM D-7904730 Mpa
tensile strength23℃ASTM D-63869 Mpa
Shear strength23℃ASTM D-73266 Mpa
Bending modulus23℃ASTM D-7903220 Mpa
Hardness (Rockwell M)ASTM D-78594
Flexural fatigue endurance limit50%RH，23℃，106周期ASTM D-67132 Mpa
Bending modulus122℃ASTM D-790755 Mpa
Elongation at Break70℃ASTM D-638180 %
tensile strength-55℃ASTM D-638101 Mpa
Impact strength of cantilever beam gap23℃ASTM D-1822250 kJ/m²
Compressive stress23℃，1%变形ASTM D-69535 Mpa
Hot deformation temperature140kg/cm2,50℃ASTM D-6210.5 %
Izod Notched Impact StrengthUnnotched23℃ASTM D-2561620 J/m
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansion104-160℃ASTM D-69614.9 10-5m/m
Linear coefficient of thermal expansion60-104℃ASTM D-69613.7 10-5m/m
Melting temperatureASTM D-2133175
Hot deformation temperature1.8MPaASTM D-648136
Linear coefficient of thermal expansion29-60℃ASTM D-69612.2 10-5m/m
Spontaneous combustionUL 94HB
thermal conductivity0.37 w/mk
Linear coefficient of thermal expansion-40-29ASTM D-69610.4 10-5m/m
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rate1.8-2.0 %
Electrical performanceTest ConditionTest MethodTest Result
Dielectric constant50%RH，23℃，102-106HzASTM D-1503.7 ohm-cm
Dielectric constant50%RH，23℃，106HzASTM D-1500.005
Dielectric strength2.3mmASTM D-14919.7 KV/mm
Arc resistance3.1mmASTM D-495220 sec
Volume resistivity23℃，0.2%含水量ASTM D-257≥14.9 ohm-cm
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.