PBT

PBT Toraycon® 1101H TORAY JAPAN

266

Unit Price:US$ 11,037 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Good appearance｜Mineral reinforcement
Application Areas:Shell
Color:--
Grade:High gloss level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	20 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Rockwell hardness	M -Sale	ISO 2039-2	80
Tensile modulus	23℃	ISO 527-2	4600 Mpa
tensile strength	Yield, 23℃	ISO 527-2	55.0 Mpa
Tensile strain	Break, 23℃	ISO 527-2	1.8 %
Bending modulus	23℃	ISO 178	4300 Mpa
bending strength	23℃	ISO 178	100 Mpa
Charpy Notched Impact Strength	23℃	ISO 179	2.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179	20 kJ/m²
bending strength	23°C	ISO 178	100 Mpa
Bending modulus	23°C	ISO 178	4300 Mpa
Tensile strain	Break,23°C	ISO 527-2	1.8 %
tensile strength	Yield,23°C	ISO 527-2	55.0 Mpa
Tensile modulus	23°C	ISO 527-2	4600 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	150 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	75.0 °C
UL flame retardant rating		UL 94	HB
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	75.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	150 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD: 3.00 mm	Internal Method	1.7 %
	Shrinkage rate	MD: 3.00 mm	Internal Method	1.8 %
		Shrinkage rate	TD:3.00mm2	Internal Method	1.7 %
		Shrinkage rate	Shrinkage rate	MD:3.00mm4	Internal Method	1.8 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale,23°C	ISO 2039-2	80

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT Toraycon® 1101H TORAY JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet