Material Description

Material Properties:Flame retardant｜High impact resistance
Application Areas:Automotive interior parts｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23℃23°C	ASTM D256	680 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃-30°C	ASTM D256	500 J/m
Instrumented impact	23℃23°C	ASTM D 3763	51 J
Instrumented impact	Instrumented impact	-30℃-30°C	ASTM D 3763	57 J

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield，50 mm/minYield，50mm/min	ASTM D638	53 Mpa
tensile strength	tensile strength	Break，50 mm/minBreak，51mm/min	ASTM D638	55 Mpa
Tensile strain Tensile strain 50mm/min	Yield，50 mm/minYield	ASTM D638	5 %
Tensile strain Tensile strain 51mm/min	Break，50 mm/minBreak	ASTM D638	120 %
Tensile modulus	50 mm/min50 mm / min	ASTM D638	2240 Mpa
bending strength	Yield，1.30 mm/min，50 mm跨度Yield，1.3 mm/min，50mmSpan	ASTM D790	86 Mpa
Bending modulus	1.30 mm/min，50 mmSpan1.3 mm/min，50mmSpan	ASTM D790	2270 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D1525	126 °C
Hot deformation temperature	3.2mm3.2mm	ASTM D 648	129 °C
Hot deformation temperature	Hot deformation temperature	6.4mm6.4mm	ASTM D 648	110 °C
Linear expansion coefficient, -40 ℃ to 40 ℃,	FlowFlow	GB 1040	0.000080 1/℃
Linear expansion coefficient, -40 ℃ to 41 ℃,	Across FlowTransverse	GB 1040	0.000080 1/℃

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.2 mmFlow	Internal Method	0.5 - 0.7 %
Shrinkage rate	Shrinkage rate	TD：3.2 mmTransverse	Internal Method	0.5 - 0.7 %
melt mass-flow rate	260℃，5.0kg260℃/5.0 kgf	ASTM D1238	13.5 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.