Material Description

Material Properties:High toughness｜transparent
Application Areas:Automotive components｜Electronic and electrical accessories
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	66.2 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	12 kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	12 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	4.0 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	2410 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2300 Mpa
elongation	Break	ASTM D638	110 %
Tensile strain	Yield	ISO 527-2/50	5.7 %
elongation	Yield	ASTM D638	6.0 %
tensile strength	Break	ISO 527-2/50	55.0 Mpa
	tensile strength	Break	ASTM D638	58.0 Mpa
		tensile strength	Yield	ISO 527-2/50	60.0 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	62.6 Mpa
Tensile strain	Break	ISO 527-2/50	110 %
Bending modulus	50.0mmSpan	ASTM D790	2410 Mpa
Bending modulus	Bending modulus		ISO 178	2300 Mpa
bending strength		ISO 178	85.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	102 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B120	140 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Vicat softening temperature	--	ISO 306/B50	139 °C
Vicat softening temperature	Vicat softening temperature		ASTM D152510	140 °C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	121 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	125 °C
		Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	133 °C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	135 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7.8E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.8E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.2E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.090 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.27 %
Shrinkage rate	TD：3.20mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	36.0 cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	250°C/1.2kg	ISO 1133	6.00 cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	39 g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.