POM

POM LNP™ LUBRICOMP™ KF006 BK SABIC INNOVATIVE US

269

Unit Price:US$ 2,588 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting｜high strength｜Glass fiber reinforced
Application Areas:Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	40 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	9200 Mpa
tensile strength	Yield	ISO 527-2/5	125 Mpa
Tensile strain	Break	ISO 527-2/5	2.9 %
Bending modulus		ISO 178	7400 Mpa
bending strength		ISO 178	163 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			4.0 hr
Temperature at the rear of the barrel			175 to 190 °C
Temperature in the middle of the barrel			195 to 205 °C
Temperature at the front of the material cylinder			210 to 220 °C
Processing (melt) temperature			200 to 215 °C
Mold temperature			80 to 110 °C
Back pressure			0.200 to 0.300 Mpa
Screw speed			30 to 60 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span	ISO 75-2/Bf	164 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span	ISO 75-2/Af	161 °C
Linear coefficient of thermal expansion	Flow : 23 to 60°C	ISO 11359-2	3.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 60°C	ISO 11359-2	9.6E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Flow	Internal Method	0.50 - 0.80 %
Shrinkage rate	Shrinkage rate	Across FlowFlow	Internal Method	0.80 - 1.1 %
Water absorption rate	24 hr, 23°C	ISO 62	0.40 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM LNP™ LUBRICOMP™ KF006 BK SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet