PA66

PA66 Amilan® CM3006G-50D TORAY PLASTICS CHENGDU

265

Unit Price:US$ 4,666 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Glass fiber reinforced
Application Areas:Automotive Applications｜Shell
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-40°C	ISO 179	12 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	15 kJ/m²
Impact strength of simply supported beam without notch	-40°C	ISO 179	85 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	90 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	-40°C	ISO 527-2	280 Mpa
	tensile strength	23°C	ISO 527-2	220 Mpa
	tensile strength	tensile strength	80°C	ISO 527-2	140 Mpa
Tensile strain	Break, -40°C	ISO 527-2	2.5 %
	Tensile strain	Break, 23°C	ISO 527-2	3.0 %
	Tensile strain	Tensile strain	Break, 80°C	ISO 527-2	5.5 %
Bending modulus	-40°C	ISO 178	15500 Mpa
	Bending modulus	23°C	ISO 178	13800 Mpa
	Bending modulus	Bending modulus	80°C	ISO 178	8600 Mpa
bending strength	-40°C	ISO 178	380 Mpa
	bending strength	23°C	ISO 178	345 Mpa
	bending strength	bending strength	80°C	ISO 178	230 Mpa
Compressive stress	-40°C	ISO 604	265 Mpa
	Compressive stress	23°C	ISO 604	195 Mpa
	Compressive stress	Compressive stress	80°C	ISO 604	120 Mpa
shear strength	23°C	ASTM D732	105 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	263 °C
Melting temperature		DSC	265 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.0E-5 - 3.0E-5 cm/cm/°C
specific heat			1500 J/kg/°C
thermal conductivity			0.42 W/m/K

Physical properties	Test Condition	Test Method	Test Result
density	23°C	ISO 1183	1.50 g/cm³
Shrinkage rate	横向Flow : 3.00 mm	Internal Method	0.50 - 0.80 %
Shrinkage rate	Shrinkage rate	Flow : 3.00 mm	Internal Method	0.20 - 0.40 %
Water absorption rate	24 hr, 23°C	ISO 62	0.40 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	4.8 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	1.0E+13 ohms·cm
Dielectric strength		IEC 60243-1	19 KV/mm
Dielectric constant	23°C, 50 Hz	IEC 60250	4.70
	Dielectric constant	23°C, 1 kHz	IEC 60250	4.50
	Dielectric constant	Dielectric constant	23°C, 1 MHz	IEC 60250	4.10
Dissipation factor	23°C, 50 Hz	IEC 60250	0.020
	Dissipation factor	23°C, 1 kHz	IEC 60250	0.020
	Dissipation factor	Dissipation factor	23°C, 1 MHz	IEC 60250	0.020

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M -Sale, 23°C	ISO 2039-2	103
Rockwell hardness	Rockwell hardness	R -Sale, 23°C	ISO 2039-2	121

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Amilan® CM3006G-50D TORAY PLASTICS CHENGDU

Material Description

Technical Data Sheet Compare

Technical Data Sheet