PC LEXAN™  FXE1414L WH9D155 SABIC INNOVATIVE NANSHA

180
  • Unit Price:US$ 4,558 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10.3MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Low temperature resistance｜transparent｜Flame retardant
  • Application Areas:Electrical appliances｜Electronic field｜Electrical field｜Household appliances
  • Color:--
  • Grade:Light diffusion level

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Dart impact23°C, Total EnergyASTM D376368.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA65 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°CISO 180/1A60 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A70 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Dart impact23°C,TotalEnergyASTM D376370.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.40 mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--2ASTM D6382030 Mpa
Tensile modulus--ISO 527-2/12000 Mpa
tensile strengthYield3ASTM D63852.0 Mpa
tensile strengthYieldISO 527-2/5052.0 Mpa
tensile strengthBreak3ASTM D63854.0 Mpa
tensile strengthBreakISO 527-2/5047.0 Mpa
elongationYield3ASTM D6385.0 %
elongationYieldISO 527-2/505.0 %
elongationBreak3ASTM D63884 %
elongationBreakISO 527-2/5075 %
Bending modulus50.0 mm Span4ASTM D7902050 Mpa
Bending modulus--5ISO 1782110 Mpa
bending strength--5,6ISO 17883.0 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79086.0 Mpa
Tensile modulusASTM D6382020 Mpa
Tensile modulusISO 527-2/12150 Mpa
tensile strengthYieldASTM D63855.5 Mpa
tensile strengthYieldISO 527-2/5057.0 Mpa
tensile strengthBreakASTM D63850.3 Mpa
tensile strengthBreakISO 527-2/5060.0 Mpa
elongationYieldASTM D6386.0 %
Tensile strainYieldISO 527-2/506.0 %
elongationBreakASTM D63898 %
Tensile strainBreakISO 527-2/50120 %
Bending modulus50.0mmSpanASTM D7902230 Mpa
Bending modulusISO 1782250 Mpa
bending strengthISO 17885.0 Mpa
bending strengthYield,50.0mmSpanASTM D79092.4 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Hopper temperature60 to 80 °C
Temperature at the rear of the barrel260 to 280 °C
Temperature in the middle of the barrel280 to 305 °C
Temperature at the front of the material cylinder295 to 315 °C
Spray nozzle temperature290 to 310 °C
Processing (melt) temperature295 to 315 °C
Mold temperature70 to 95 °C
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648121 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8ISO 75-2/Af118 °C
Vicat softening temperature--ASTM D15259138 °C
Vicat softening temperature--ISO 306/B120146 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8317.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8316.7E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-28.2E-5 cm/cm/°C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648139 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648124 °C
Hot deformation temperature1.8MPa,Unannealed,100mmSpanISO 75-2/Ae128 °C
Vicat softening temperatureASTM D152510145 °C
Vicat softening temperature--ISO 306/B50145 °C
Vicat softening temperature--ISO 306/B120146 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8317E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：23to80°CISO 11359-27.2E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8317.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27.2E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2 kgASTM D123811 g/10 min
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113310.0 cm3/10min
Shrinkage rate3.20 mm，FlowInternal Method0.40 - 0.80 %
Water absorption rateSaturation, 23°CISO 620.17 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.070 %
Water absorption rateSaturation,23°CISO 620.35 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
melt mass-flow rate300°C/1.2kgASTM D123810 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11339.00 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.40-0.80 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.