Material Description

Material Properties:High impact resistance
Application Areas:Phone｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8 mm	UL 94	V-2
	UL flame retardant rating	2.5 mm	UL 94	V-2
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-2

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--3	ASTM D638	2000 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/50	2000 Mpa
tensile strength	Yield3	ASTM D638	59.0 Mpa
	tensile strength	Yield	ISO 527-2/50	55.0 Mpa
		tensile strength	Break3	ASTM D638	59.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	69.0 Mpa
elongation	Break3	ASTM D638	110 %
elongation	elongation	Break	ISO 527-2/50	110 %
Bending modulus	--4	ASTM D790	2000 Mpa
Bending modulus	Bending modulus	--5	ISO 178	2100 Mpa
bending strength	--4	ASTM D790	83.0 Mpa
bending strength	bending strength	--5	ISO 178	84.0 Mpa

injection	Test Condition	Test Method	Test Result
Hot air dryer			100 °C
Vacuum drying machine			100 °C
Hot air dryer			2.0 to 4.0 hr
Vacuum drying machine			2.0 to 6.0 hr
Suggested maximum moisture content			< 0.050 %
Temperature at the rear of the barrel			240 to 250 °C
Temperature in the middle of the barrel			260 to 270 °C
Temperature at the front of the material cylinder			280 to 310 °C
Spray nozzle temperature			290 to 310 °C
Mold temperature			40 to 100 °C
Injection pressure			49.0 to 245 Mpa
Back pressure			0.490 to 1.96 Mpa
Screw speed			50 to 150 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	136 °C
	Hot deformation temperature	0.45 MPa, Annealed, 4.00 mm	ISO 75-2/B	136 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	121 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Annealed, 4.00 mm	ISO 75-2/A	125 °C
Vicat softening temperature	--	ISO 306/B50	141 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	145 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	250°C/10.0 kg	ASTM D1238	18 g/10 min
Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.40 - 0.70 %
	Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.40 - 0.70 %
		Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.40 - 0.70 %
		Shrinkage rate	Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.40 - 0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	120
Rockwell hardness	Rockwell hardness	R -Sale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.