PC LEXAN™  SLX2271T NA9E166T SABIC INNOVATIVE SINGAPHORE

325
  • Unit Price:US$ 4,985 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Aging resistance｜UV resistance｜Antistatic
  • Application Areas:Electronic and Electrical Applications｜Lighting applications｜Plastic bag｜Outdoor applications｜Lawn garden equipment
  • Color:--
  • Grade:High liquidity level

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
Refractive indexISO 4891.590
transmissivity2540μmASTM D100389.0 %
turbidity2540μmASTM D10030.60 %
impact performanceTest ConditionTest MethodTest Result
Dart impact23°C,TotalEnergyASTM D376380.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA15 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA65 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A65 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.0mmUL 94V-2
Burning wire flammability index1.6mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
Hot filament ignition temperature2.0mmIEC 60695-2-13825 °C
Hot filament ignition temperature2.5mmIEC 60695-2-13825 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13825 °C
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthYieldASTM D63865.0 Mpa
tensile strengthYieldISO 527-2/5067.0 Mpa
tensile strengthBreakASTM D63867.0 Mpa
tensile strengthBreakISO 527-2/5070.0 Mpa
elongationYieldASTM D6386.0 %
Tensile strainYieldISO 527-2/506.0 %
elongationBreakASTM D638>100 %
Tensile strainBreakISO 527-2/50>100 %
Bending modulus50.0mmSpanASTM D7902450 Mpa
Bending modulusISO 1782450 Mpa
Tensile modulusASTM D6382400 Mpa
Tensile modulusISO 527-2/12300 Mpa
bending strengthISO 17896.0 Mpa
bending strengthYield,50.0mmSpanASTM D79096.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648124 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af124 °C
Vicat softening temperatureASTM D152510139 °C
Vicat softening temperature--ISO 306/B50139 °C
Vicat softening temperature--ISO 306/B120140 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：-40to40°CASTME8317E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-27E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8317E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-27E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2kgASTM D123818 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113316.0 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Water absorption rateSaturation,23°CISO 620.35 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Outdoor applicabilityUL 746Cf2
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.