Plastic Raw Materials
PBT

PBT Cristin®  LW9030FR BK851 DUPONT USA

215
  • Unit Price:US$ 3,796 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Low warpage｜Flame retardant｜Filler: Glass fiber reinforced material｜30% filler by weight
  • Application Areas:Electronic and electrical components
  • Color:--
  • Grade:Flame retardant grade

Material Certification

UL

Technical Data Sheet

Other performanceTest ConditionTest MethodTest Result
Extreme Oxygen IndexISO 4589-119 %
impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA10 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU65 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU60 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A8.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A8.0 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U50 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U50 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Burning rate1.00mmISO 379542 mm/min
UL flame retardant rating1.5mmUL 94HB
UL flame retardant rating3.0mmUL 94HB
UL flame retardant rating1.5mmIEC 60695-11-10,-20HB
UL flame retardant rating3.0mmIEC 60695-11-10,-20HB
Extreme Oxygen IndexISO 4589-219 %
FMVSS flammabilityFMVSS302B
mechanical propertiesTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch23 ℃, Type 1, EdgewiseISO 17960 KJ/m
Charpy Notched Impact Strength-30 ℃, Type 1, Edgewise, Notch AISO 1799.3 KJ/m
Charpy Notched Impact Strength23℃, Type 1, Edgewise, Notch AISO 17910 KJ/m
Impact strength of cantilever beam gap23℃, Type 1, Notch AISO 18010 KJ/m
Tensile stress23℃，BreakISO 527-1130 MPa
Tensile strain23℃，BreakISO 527-12.5 %
Tensile creep modulus1hISO 899-19000 MPa
Tensile creep modulus1000hISO 899-17300 MPa
Tensile modulus23℃ISO 527-19500 MPa
bending strength23℃ISO 178190 MPa
Impact strength of simply supported beam without notch-30 ℃, Type 1, EdgewiseISO 17966 KJ/m
Tensile modulusISO 527-29500 Mpa
tensile strengthBreakISO 527-2130 Mpa
Tensile strainBreakISO 527-22.5 %
Tensile creep modulus1hrISO 899-19000 Mpa
Tensile creep modulus1000hrISO 899-17300 Mpa
Bending modulusISO 1788500 Mpa
bending strengthISO 178190 Mpa
thermal performanceTest ConditionTest MethodTest Result
UL flame retardant rating1.50 mmUL 94HB
UL flame retardant rating3.00 mmUL 94HB
Melting temperatureISO 3146225 ℃
Linear coefficient of thermal expansion平行Flow，23 to 55°C (73 to 130°F)ISO 11359-10.000100 cm/cm/°C
Linear coefficient of thermal expansion垂直Flow，23 to 55°C (73 to 130°F)ISO 11359-10.000025 cm/cm/°C
Hot deformation temperature0.45 Mpa，UnannealedISO 75B-1215 ℃
Hot deformation temperature1.80 Mpa，UnannealedISO 75B-1182 ℃
Glass transition temperatureISO 11357-2120 °C
Vicat softening temperatureISO 306/B50150 °C
Melting temperatureISO 11357-3225 °C
Linear coefficient of thermal expansionMDISO 11359-22.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTDISO 11359-21E-04 cm/cm/°C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B215 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A170 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rate23C/59RHISO 620.24 %
Water absorption rateSat/23CISO 620.72 %
Shrinkage rateAcross FlowISO 294-40.65 %
Shrinkage rateFlowISO 294-40.25 %
densityISO 11831.44
Shrinkage rateMDISO 294-40.20 %
Shrinkage rateMD:80°C,48hrISO 294-40.15 %
Water absorption rateSaturation,23°C,2.00mmISO 620.72 %
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.24 %
Top out temperature170 °C
Shrinkage rateTD:80°C,48hrISO 294-40.20 %
Shrinkage rateTDISO 294-40.70 %
Melt Volume Flow Rate (MVR)250°C/5.0kgISO 113310.0 cm3/10min
densityISO 11831.44 g/cm³
ThermalConductivityofMelt0.26 W/m/K
SpecificHeatCapacity of Melt1900 J/kg/°C
MediumDensity1.28 g/cm³
Electrical performanceTest ConditionTest MethodTest Result
Relative permittivity1MHzIEC 602503.60
Dissipation factor100HzIEC 602502.4E-03
Dissipation factor1MHzIEC 602500.017
Compared to the anti leakage trace indexIEC 60112PLC 1
Relative permittivity100HzIEC 602503.90
Surface resistivityIEC 600931E+14 ohms
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dielectric strengthIEC 60243-136 KV/mm
Supplementary InformationTest ConditionTest MethodTest Result
EmissionofOrganicCompoundsVDA27790.0 µgC/g
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.