PPO NORYL™  ENG265-8746S NR4N77 SABIC INNOVATIVE US

219
  • Unit Price:US$ 3,797 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Thermal stability｜Glass fiber reinforced
  • Application Areas:medical care｜Profile｜Pipe fittings
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of cantilever beam gap-30°CISO 180/1A8.7 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A13 kJ/m²
Dart impact23°C,TotalEnergyASTM D376339.0 J
Dart impact-40°CASTM D30295.42 J
Dart impact-30°CASTM D302925.8 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
elongationBreakASTM D63828 %
Tensile strainBreakISO 527-227 %
Bending modulus50.0mmSpan4ASTM D7902550 Mpa
Bending modulus100mmSpan5ASTM D7902450 Mpa
Bending modulusISO 1782500 Mpa
bending strengthISO 17895.0 Mpa
bending strengthYield,50.0mmSpan4ASTM D79089.0 Mpa
bending strengthYield,100mmSpan5ASTM D79088.0 Mpa
Tensile modulusASTM D6382400 Mpa
Tensile modulusISO 527-2/12550 Mpa
tensile strengthYieldASTM D63856.0 Mpa
tensile strengthYieldISO 527-255.0 Mpa
tensile strengthBreakASTM D63850.0 Mpa
tensile strengthBreakISO 527-250.0 Mpa
elongationYieldASTM D6383.3 %
Tensile strainYieldISO 527-23.1 %
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648132 °C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648137 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648118 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648126 °C
Vicat softening temperature--ISO 306/B50137 °C
Vicat softening temperature--ISO 306/B120141 °C
Linear coefficient of thermal expansionMD：-40to95°CASTME8315.9E-05 cm/cm/°C
RTI ElecUL 746105 °C
RTI ImpUL 74690.0 °C
RTI StrUL 746105 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Water absorption rate24hrASTM D5700.060 %
melt mass-flow rate280°C/5.0kgASTM D12388.5 g/10min
Melt Volume Flow Rate (MVR)280°C/5.0kgISO 11338.70 cm3/10min
Electrical performanceTest ConditionTest MethodTest Result
Dielectric constant60HzASTM D1502.65
Dissipation factor50HzASTM D1504E-04
Dissipation factor60HzASTM D1504E-04
Arc resistanceASTM D495PLC7
Compared to the anti leakage trace indexCTIUL 746PLC 3
High arc combustion indexHAIUL 746PLC 0
High voltage arc tracing rateHVTRUL 746PLC 4
Hot wire ignitionHWIUL 746PLC 2
Dielectric strength3.20mm,inOilASTM D14920 KV/mm
Dielectric constant50HzASTM D1502.65
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785119
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.