PC LEXAN™  EXL5689 WH7B221 SABIC INNOVATIVE NANSHA

223
  • Unit Price:US$ 4,421 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Dart impact23°C,TotalEnergyASTM D376340.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA15 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA30 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A25 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.75mmUL 94HB
UL flame retardant rating1.2mmUL 94V-1
UL flame retardant rating1.5mmUL 94V-0
Burning wire flammability index1.1mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
Hot filament ignition temperature2.0mmIEC 60695-2-13825 °C
Hot filament ignition temperature2.5mmIEC 60695-2-13825 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13825 °C
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthYieldISO 527-2/554.0 Mpa
tensile strengthBreakASTM D63844.0 Mpa
tensile strengthBreakISO 527-2/546.0 Mpa
elongationYieldASTM D6384.4 %
Tensile strainYieldISO 527-2/54.4 %
elongationBreakASTM D63815 %
Tensile strainBreakISO 527-2/513 %
Bending modulus50.0mmSpanASTM D7903150 Mpa
Bending modulusISO 1783400 Mpa
bending strengthISO 17896.0 Mpa
Tensile modulusASTM D6383500 Mpa
Tensile modulusISO 527-2/13600 Mpa
tensile strengthYieldASTM D63855.0 Mpa
bending strengthYield,50.0mmSpanASTM D79097.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,Unannealed,100mmSpanISO 75-2/Ae132 °C
Vicat softening temperatureASTM D152510146 °C
Vicat softening temperature--ISO 306/B50145 °C
Vicat softening temperature--ISO 306/B120146 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：-40to40°CASTME8314.7E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-24.7E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8317E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-27E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2kgASTM D12389.0 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11338.00 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.20-0.60 %
Water absorption rateSaturation,23°CISO 620.35 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Electrical performanceTest ConditionTest MethodTest Result
Compared to the anti leakage trace indexCTIUL 746PLC 3
Compared to the anti leakage trace indexIEC 60112PLC 3
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.