PBT Toraycon® 1401X06 TORAY JAPAN

378

Unit Price:US$ 3,053 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
41MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Automotive sector｜Shell
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			非增强标准级

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-40°C	ISO 179	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	240 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	HB

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	23℃·24hr	ASTM D-570	0.08 %

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256/ISO 179	45 kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap		ASTM D256/ISO 179	35 kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap		ASTM D256/ISO 179	nb kg·cm/cm(J/M)ft·lb/in
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	120 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	100 %
tensile strength		ASTM D638/ISO 527	55 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	M75
Bending modulus		ASTM D790/ISO 178	2.5 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	85 kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	23℃	ASTM D-790	900 kg/cm
tensile strength	23℃	ASTM D-638	600 kg/cm
Bending modulus	23℃	ASTM D-790	26 kg/cm
Rockwell hardness		ASTM D-785	75 M标度
Elongation at Break	23℃	ASTM D-638	15 %
Impact strength of cantilever beam gap	Unnotched，23℃	ASTM D-256	不破裂 kg·cm/cm
	Impact strength of cantilever beam gap	Unnotched，-40℃	ASTM D-256	120 kg·cm/cm
		Impact strength of cantilever beam gap	Notched，23℃	ASTM D-256	4.4 kg·cm/cm
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Notched，-40℃	ASTM D-256	3.5 kg·cm/cm
compressive strength	23℃	ASTM D-695	900 kg/cm
Tensile modulus	23°C	ISO 527-2	2700 Mpa
tensile strength	Yield,23°C	ISO 527-2	55.0 Mpa
Tensile strain	Break,23°C	ISO 527-2	30 %
Bending modulus	23°C	ISO 178	2500 Mpa
bending strength	23°C	ISO 178	90.0 Mpa
Friction coefficient			0.17
Friction coefficient vs. Metal		SuzukiMethod	0.13

thermal performance	Test Condition	Test Method	Test Result
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	60 1.8Mpa ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	9.4*10^-5 mm/mm.℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ASTM D-696	9.4 cm/cm℃×10
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	150 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	60.0 °C
Linear coefficient of thermal expansion	MD：-30to100°C	ISO 11359-2	1.1E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792/ISO 1183	1.31
Water absorption rate		ASTM D570/ISO 62	0.08 %
Taber abraser	1.000g·CS-17	ASTM D-1044	10 毫克/1.000m
Shrinkage rate	80×80×3板材		1.7-2.3 %
Friction coefficient	金属	ASTM D-1894	0.13
Friction coefficient	Friction coefficient	本身	ASTM D-1894	0.17
Hot deformation temperature	4.6kg/cm	ASTM D-648	154 °C
Hot deformation temperature	Hot deformation temperature	18.6kg/cm	ASTM D-648	58 °C
Shrinkage rate	TD:3.00mm2	Internal Method	2.3 %
Shrinkage rate	Shrinkage rate	MD:3.00mm4	Internal Method	1.7 %
Water absorption rate	23°C,24hr	ISO 62	0.080 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant		ASTM D150/IEC 60250	3.3
Volume resistivity		ASTM D257/IEC 60093	4.0*10^14 Ω.cm
Volume resistivity	Volume resistivity		ASTM D-257	4.0 cm×10
Dielectric strength	短时·23℃·1/8时	ASTM D-149	17 KV/mm
Arc resistance		ASTM D-495	144 秒
Dielectric constant	23°C,1kHz	IEC 60250	3.30
Dissipation factor	23°C,50Hz	IEC 60250	2E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	0.020
Arc resistance		IEC 60950	144 sec
Compared to the anti leakage trace index	CTI	UL 746	PLC 0
Volume resistivity		IEC 60093	8E+16 ohms·cm
Dielectric strength		IEC 60243-1	17 KV/mm
Dielectric constant	23°C,50Hz	IEC 60250	3.30

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale,23°C	ISO 2039-2	77

Supplementary Information	Test Condition	Test Method	Test Result
BarFlowLength	250°C,1.00mm	Internal Method	103 mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.