PET Rynite® 935 NC010 DUPONT USA

244

Unit Price:US$ 2,933 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
29.1MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜High temperature resistance
Application Areas:Automotive Applications｜household electrical appliances
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			刚性良好抗老化性良好抗弯曲
Color			自然色
purpose			电气/电子应用领域汽车领域应用

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	20 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	25 kJ/m²

machinability	Test Condition	Test Method	Test Result
Melt Temperature			280-300 %

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ISO 4589-2	21 %
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	1E-04 g
Burning rate	1.00mm	ISO 3795	<100 mm/min
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	10200 Mpa
tensile strength	Break	ISO 527-2	85.0 Mpa
Tensile strain	Break	ISO 527-2	2.0 %
Tensile creep modulus	1hr	ISO 899-1	9350 Mpa
compressive strength		ASTM D695	141 Mpa
tensile strength		ASTM D638	89.6 Mpa
Tensile modulus		ASTM D638	9930 Mpa
Bending modulus		ASTM D790	9600 Mpa
bending strength		ASTM D790	141 Mpa
Elongation at Break		ASTM D638	2.0 %
Impact strength of cantilever beam gap		ASTM D256	43 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256	64 J/m
Suspended wall beam without notch impact strength		ASTM D256	425 J/m
Tensile creep modulus	1000hr	ISO 899-1	7690 Mpa
Bending modulus		ISO 178	9100 Mpa
Elongation at Break		ASTM D638/ISO 527	2.0 %
Tensile modulus		ASTM D412/ISO 527	10200 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	75
Bending modulus		ASTM D790/ISO 178	9100 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	141 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ISO 306/B50	205 °C
Melting temperature		ISO 11357-3	252 °C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	1.6E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	2.6E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	5.2E-05 cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	5.3E-05 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	1.4E-07 m²/s
Hot deformation temperature	66 psi， Unannealed	ASTM D648	241 °C
Hot deformation temperature	Hot deformation temperature	264 psi，Unannealed	ASTM D648	215 °C
Linear coefficient of thermal expansion		ASTM E831	0.000016 cm/cm/ ℃
Melting temperature			252 °C
UL flame retardant rating		UL 94	HB
Extreme Oxygen Index		ASTM D2863	-- %
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	235 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200 °C
	Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	235 ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	280°C/5.0kg	ISO 1133	5.00 cm3/10min
Shrinkage rate	TD	ISO 294-4	0.70 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.30 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.83 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.13 %
MediumDensity			1.32 g/cm³
Top out temperature			170 °C
SpecificHeatCapacity of Melt			1790 J/kg/°C
Shrinkage rate	3.20 mm，平行Flow	ASTM D955	0.0035 cm/cm
Shrinkage rate	Shrinkage rate	3.20 mm，垂直	ASTM D955	0.0065 cm/cm
ThermalConductivityofMelt			0.32 W/m/K
density		ASTM D792/ISO 1183	1.58

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity		IEC 60093	1E+15 ohms·cm
Dielectric strength		IEC 60243-1	39 KV/mm
Relative permittivity	100Hz	IEC 60250	4.50
Relative permittivity	Relative permittivity	1MHz	IEC 60250	4.10
Dissipation factor	100Hz	IEC 60250	0.030
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.014
Compared to the anti leakage trace index		IEC 60112	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale	ISO 2039-2	75
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	115

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PET Rynite® 935 NC010 DUPONT USA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet