Plastic Raw Materials
PET

PET Rynite®  FR530 DUPONT USA

483
  • Unit Price:US$ 4,046 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    155MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:enhance｜Glass fiber reinforced｜wear resistant｜High rigidity｜High temperature resistance｜Filler: Glass fiber reinforced material｜30% filler by weight
  • Application Areas:Electrical field｜Electronic field｜Household appliances｜Household appliances｜Automotive sector
  • Color:--
  • Grade:Injection grade

Material Certification

UL
SGS

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA10 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU40 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU40 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.35mmUL 94V-0
UL flame retardant rating1.5mmUL 94V-0
UL flame retardant rating0.35mmIEC 60695-11-10,-20V-0
UL flame retardant rating1.5mmIEC 60695-11-10,-20V-0
Extreme Oxygen IndexISO 4589-233 %
FMVSS flammabilityFMVSS302DNI
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-211500 Mpa
tensile strengthBreakISO 527-2135 Mpa
Tensile strainBreakISO 527-22.0 %
Tensile creep modulus1hrISO 899-111200 Mpa
Tensile creep modulus1000hrISO 899-19700 Mpa
Bending modulusISO 17810500 Mpa
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionMD：-40to23°CISO 11359-22.2E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：--ISO 11359-29.2E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to23°CISO 11359-26.8E-05 cm/cm/°C
RTI Elec0.40mmUL 746155 °C
RTI Elec0.75mmUL 746155 °C
RTI Elec1.5mmUL 746155 °C
RTI Elec3.0mmUL 746155 °C
RTI Imp0.40mmUL 746155 °C
RTI Imp0.75mmUL 746155 °C
RTI Imp1.5mmUL 746155 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B243 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A225 °C
Vicat softening temperatureISO 306/B50220 °C
Melting temperatureISO 11357-3252 °C
Linear coefficient of thermal expansionMD：--ISO 11359-21.9E-05 cm/cm/°C
RTI Imp3.0mmUL 746155 °C
RTI Str0.40mmUL 746155 °C
RTI Str0.75mmUL 746155 °C
RTI Str1.5mmUL 746155 °C
RTI Str3.0mmUL 746155 °C
RTI StrEffectiveThermalDiffusivityUL 7461.1E-07 m²/s
Physical propertiesTest ConditionTest MethodTest Result
densityISO 11831.68 g/cm³
Melt Volume Flow Rate (MVR)280°C/2.16kgISO 11336.00 cm3/10min
Shrinkage rateTDISO 294-40.80 %
Shrinkage rateMDISO 294-40.20 %
Water absorption rateSaturation,23°C,2.00mmISO 620.75 %
Water absorption rateEquilibrium,23°C,2.00mm,50%RHISO 620.15 %
Top out temperature170 °C
Electrical performanceTest ConditionTest MethodTest Result
Relative permittivity1MHzIEC 602504.30
Dissipation factor100HzIEC 602507E-03
Dissipation factor1MHzIEC 602500.013
Compared to the anti leakage trace indexCTIUL 746PLC 2
Compared to the anti leakage trace indexIEC 60112PLC 3
Surface resistivityIEC 600931E+14 ohms
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Dielectric strengthIEC 60243-139 KV/mm
Relative permittivity100HzIEC 602504.80
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.