PC LEXAN™  EXL1492C NA8D017 SABIC INNOVATIVE US

169
  • Unit Price:US$ 3,577 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    16MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility｜Ductility at low temperature｜Short molding cycle
  • Application Areas:Electronic and Electrical Applications｜Aerospace Applications｜lens
  • Color:--
  • Grade:Extrusion grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
Impact strength of cantilever beam gap23°CISO 180/1A70 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A60 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA65 kJ/m²
Dart impact23°C,TotalEnergyASTM D376370.0 J
flammabilityTest ConditionTest MethodTest Result
Burning wire flammability index0.8mmIEC 60695-2-12850 °C
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13875 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13875 °C
Extreme Oxygen IndexISO 4589-237 %
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-2/12150 Mpa
Tensile modulusASTM D6382020 Mpa
tensile strengthYieldASTM D63855.5 Mpa
tensile strengthYieldISO 527-2/5057.0 Mpa
tensile strengthBreakASTM D63850.3 Mpa
tensile strengthBreakISO 527-2/5060.0 Mpa
elongationYieldASTM D6386.0 %
Tensile strainYieldISO 527-2/506.0 %
elongationBreakASTM D63898 %
Tensile strainBreakISO 527-2/50120 %
Bending modulus50.0mmSpanASTM D7902230 Mpa
Bending modulusISO 1782250 Mpa
bending strengthISO 17885.0 Mpa
bending strengthYield,50.0mmSpanASTM D79092.4 Mpa
thermal performanceTest ConditionTest MethodTest Result
Vicat softening temperature--ISO 306/B120146 °C
Vicat softening temperature--ISO 306/B50145 °C
Vicat softening temperatureASTM D152510145 °C
Hot deformation temperature1.8MPa,Unannealed,100mmSpanISO 75-2/Ae128 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648124 °C
Hot deformation temperature0.45MPa,Unannealed,100mmSpanISO 75-2/Be140 °C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648139 °C
Linear coefficient of thermal expansionTD：-40to40°CASTME8317.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27.2E-05 cm/cm/°C
Ball Pressure Test125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：-40to40°CASTME8317E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：23to80°CISO 11359-27.2E-05 cm/cm/°C
RTI ElecUL 746130 °C
RTI ImpUL 746120 °C
RTI StrUL 746125 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Water absorption rateSaturation,23°CISO 620.35 %
Shrinkage rateTD：3.20mmInternal Method0.40-0.80 %
Shrinkage rateMD：3.20mmInternal Method0.40-0.80 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11339.00 cm3/10min
melt mass-flow rate300°C/1.2kgASTM D123810 g/10min
Electrical performanceTest ConditionTest MethodTest Result
Dielectric strength0.800mm,inOilASTM D14916 KV/mm
Dielectric constant100HzASTM D1502.68
Dielectric constant1MHzASTM D1502.64
Dissipation factor100HzASTM D1501.2E-03
Dissipation factor1MHzASTM D1509.3E-03
Surface resistivityASTM D257>1.0E+15 ohms
Volume resistivityASTM D257>1.0E+15 ohms·cm
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-SaleASTM D785121
Rockwell hardnessL-SaleASTM D78589
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.