POM LNP™ THERMOCOMP™ KFX-1003 SABIC INNOVATIVE US

205

Unit Price:US$ 3,365 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Low temperature resistance｜Filler: Glass fiber reinforced material｜10% filler by weight
Application Areas:Electronic and electrical components｜Laptop case
Color:--
Grade:Demoulding grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Impact Energy		ISO 6603-2	1.45 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	33 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.3 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	137 Mpa
bending strength	bending strength		ASTM D790	129 Mpa
Bending modulus		ISO 178	5400 Mpa
Bending modulus	Bending modulus		ASTM D790	4620 Mpa
Tensile strain	Break	ISO 527-2	3.4 %
elongation	Break	ASTM D638	3.2 %
tensile strength	Break	ISO 527-2	86.4 Mpa
tensile strength	tensile strength	Break	ASTM D638	84.5 Mpa
Tensile modulus		ISO 527-2/1	5400 Mpa
Tensile modulus	Tensile modulus		ASTM D638	4760 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	161 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	162 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	164 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.35 %
Water absorption rate	Water absorption rate	24hr,50%RH	ASTM D570	0.19 %
Shrinkage rate	MD:24hr	ISO 294-4	1.2 %
	Shrinkage rate	TD:24hr	ISO 294-4	1.3 %
		Shrinkage rate	TD：24hr	ASTM D955	1.3 %
		Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	1.2 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM LNP™ THERMOCOMP™ KFX-1003 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet