PC LEXAN™  1132T BK SABIC INNOVATIVE US

164
  • Unit Price:US$ 3,507 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    24MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Middle flow｜Thermal stability
  • Application Areas:Lighting applications｜Plastic bag
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
transmissivity2540μmASTM D100382.0 %
turbidity2540μmASTM D10033.0 %
impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Dart impact23°C,TotalEnergyASTM D376374.9 J
Charpy Notched Impact Strength-30°CISO 179/1eA45 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA65 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°CISO 180/1A40 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A55 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Hot filament ignition temperature0.8mmIEC 60695-2-13850 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13850 °C
UL flame retardant rating1.5mmUL 94HB
Burning wire flammability index3.0mmIEC 60695-2-12960 °C
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthYieldASTM D63858.6 Mpa
tensile strengthYieldISO 527-2/5057.8 Mpa
tensile strengthBreakASTM D63857.1 Mpa
tensile strengthBreakISO 527-2/5056.8 Mpa
elongationYieldASTM D6385.7 %
Tensile strainYieldISO 527-2/505.4 %
elongationBreakASTM D638120 %
Tensile strainBreakISO 527-2/50120 %
Bending modulus50.0mmSpanASTM D7902250 Mpa
Bending modulusISO 1782150 Mpa
Tensile modulusASTM D6382260 Mpa
Tensile modulusISO 527-2/12340 Mpa
bending strengthISO 17889.5 Mpa
bending strengthYield,50.0mmSpanASTM D79094.8 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648122 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af117 °C
Vicat softening temperatureASTM D152510139 °C
Vicat softening temperature--ISO 306/B50139 °C
Vicat softening temperature--ISO 306/B120140 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：-40to95°CASTME8317.5E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：23to80°CISO 11359-27.5E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to95°CASTME8317.6E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27.6E-05 cm/cm/°C
RTI ElecUL 746130 °C
RTI StrUL 746130 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2kgASTM D123820 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113319.0 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.40-0.80 %
Shrinkage rateTD：3.20mmInternal Method0.40-0.80 %
Water absorption rateSaturation,23°CISO 620.12 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.090 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivityASTM D257>1.0E+15 ohms
Volume resistivityASTM D257>1.0E+15 ohms·cm
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessL-SaleISO 2039-289
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.