PC LEXAN™  HFD1910-NA9E108T SABIC INNOVATIVE NANSHA

84
  • Unit Price:US$ 4,284 /MT
  • Packaging Specification:
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility｜Hydrolysis resistance
  • Application Areas:Electrical applications｜Automotive Applications｜Mechanical accessories
  • Color:--
  • Grade:Cold resistant grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
Refractive indexASTM D5421.582
transmissivity2540μmASTM D100388.0 %
turbidity2540μmASTM D1003<1.0 %
impact performanceTest ConditionTest MethodTest Result
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A55 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
Suspended wall beam without notch impact strength23°CISO 180/1UNoBreak
Dart impact23°C,TotalEnergyASTM D376356.0 J
Multi axis Instrumented Impact EnergyISO 6603-292.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA11 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA60 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.50mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-2/12200 Mpa
tensile strengthYieldASTM D63860.0 Mpa
tensile strengthYieldISO 527-2/5061.0 Mpa
tensile strengthBreakASTM D63857.0 Mpa
tensile strengthBreakISO 527-2/5056.0 Mpa
elongationYieldASTM D6385.5 %
Tensile strainYieldISO 527-2/506.0 %
elongationBreakASTM D638110 %
Tensile strainBreakISO 527-2/50100 %
Bending modulus50.0mmSpanASTM D7902280 Mpa
Bending modulusISO 1782200 Mpa
bending strengthISO 17890.0 Mpa
bending strengthYield,50.0mmSpanASTM D790100 Mpa
Tensile modulusASTM D6382300 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648124 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648110 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af120 °C
Vicat softening temperatureASTM D152510141 °C
Vicat softening temperature--ISO 306/B50135 °C
Vicat softening temperature--ISO 306/B120136 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：-40to40°CASTME8318E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-28E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8318E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-28E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2kgASTM D123855 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113351.0 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Water absorption rateSaturation,23°CISO 620.30 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785120
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.